Skip Navigation LinksARC5 ARC 5

  • Cures on damp surfaces
    • Surface tolerant for faster and easier application
  • 100% solids; no VOCs; no free isocyanates
    • Enhances safe use
  • Convenient 4:1 by weight and volume mix ratio
    • Simplifies mixing and application
  • Low temperature cure capable
    • ​Cures down to 4°C (40°F)
  • Achieves strong adhesion to dry and damp surfaces
    • Offers substantial versatility in application​​
Pitted metal surfaces
Leaking pipes
Holed floating tank roofs
Flange faces
Cracked valves
Scored hydraulic rams and pistons
Leaking ductwork
Holed pump casings​
​ ​ ​

Composition MatrixA modified epoxy resin reacted with an aliphatic polyamine curing agent
​​Composit​ion ​Reinforcement(Proprietary​)Blend of fine ceramic particles designed for abrasion and corrosion resistance
​​​Cured Density​​​​​1.6 gm/cc​100 lb/ cu.ft.
​Tensile Adhesion(ASTM D 4541246.8 kg/cm2 (24.2 MPa)3,510 psi
Compressive Strength(ASTM D 695)630 kg/cm29,000 psi
Flexural Strength(ASTM D 790)270 kg/cm23,900 psi
Flexural Modulus(ASTM D 790)3.0 x 104 kg/cm24.2 x 105 psi
Tensile Strength(ASTM D 638)180 kg/cm22,580 psi
Shore D Durometer Hardness(ASTM D 2240)90
Vertical Sag Resistance at 21°C (70°F) and 6 mm (1/4") No sag
Maximum Temperature(Dependent on Service)​Wet Service
Dry Service
Click Here for Foreign Language Literature



SDS (Part B) - ARC 5 (English) (Part B) - ARC 5 (English)
Application Instructions - ARC 5 (English) Instructions - ARC 5 (English)
Product Datasheet - ARC 5 (English) Datasheet - ARC 5 (English)
SDS (Part A) - ARC 858, ARC 5 (English) (Part A) - ARC 858, ARC 5 (English)

Click Here for Foreign Language Literature



ARC Case Study 137: General Industry - Fire Water Tank Valve Tank_Valve.pdfARC Case Study 137: General Industry - Fire Water Tank Valve

Nominal, based on a 3 mm (120 mils) thickness

  • 250 g kit covers 521 cm2 (80 in2)
    ​Note: Components are pre-measured and pre-weighed.
    Each kit includes mixing and application instructions plus tools.

Available Colors